Astm C642 Density Absorption Voids In Hardened Concrete -
| Property | Typical Value | | :--- | :--- | | Dry Density | 125 – 155 lb/ft³ (2000 – 2480 kg/m³) | | Absorption | 4 – 8% | | Permeable Voids | 12 – 18% |
Because time is not the same as energy. A sample soaked at room temperature for a month will still have trapped air in pores smaller than 0.1 microns. Boiling forces water into those nano-pores. ASTM C642 is deliberately aggressive. It measures permeable voids—the voids that actually connect to the surface and can transport water. astm c642 density absorption voids in hardened concrete
Armed with ASTM C642 data, the owner rejected the deck. The contractor demolished and repoured. The test cost less than $500 per core. The replacement cost $2.3 million. Concrete is not a rock. It is a manufactured geology, and its performance depends entirely on the geometry of its emptiness. ASTM C642 is not glamorous. It involves no high-speed cameras or finite element models. It is just a scale, an oven, a boiling pot, and a calculator. | Property | Typical Value | | :---
Here is how the test unfolds in a typical materials laboratory. A technician cuts a slice from a concrete core or a beam. They avoid the top 1-inch surface (which has different properties due to finishing) and any reinforcing bars. The ideal specimen is a cylinder or a sawn cube with a volume between 350 and 700 cm³. ASTM C642 is deliberately aggressive
| Property | Typical Value | | :--- | :--- | | Dry Density | 125 – 155 lb/ft³ (2000 – 2480 kg/m³) | | Absorption | 4 – 8% | | Permeable Voids | 12 – 18% |
Because time is not the same as energy. A sample soaked at room temperature for a month will still have trapped air in pores smaller than 0.1 microns. Boiling forces water into those nano-pores. ASTM C642 is deliberately aggressive. It measures permeable voids—the voids that actually connect to the surface and can transport water.
Armed with ASTM C642 data, the owner rejected the deck. The contractor demolished and repoured. The test cost less than $500 per core. The replacement cost $2.3 million. Concrete is not a rock. It is a manufactured geology, and its performance depends entirely on the geometry of its emptiness. ASTM C642 is not glamorous. It involves no high-speed cameras or finite element models. It is just a scale, an oven, a boiling pot, and a calculator.
Here is how the test unfolds in a typical materials laboratory. A technician cuts a slice from a concrete core or a beam. They avoid the top 1-inch surface (which has different properties due to finishing) and any reinforcing bars. The ideal specimen is a cylinder or a sawn cube with a volume between 350 and 700 cm³.